Dear Phil Hamling  

I was glad to see your works. They are very beautiful. The color is so wonderful. Thank you very much for your commenting my works highly. Sometimes I use ferror 3110, especially to make fan-shape or leaf-shape crystals, I like to use 3110.
Works of page(http://krceramics.com/zbxe/?mid=cry...stStyle=gallery) is what I made using 3110 with feric oxide 2.0%. If you attempt to use another body-clay-including much feldspar, you would be able to make different-shape crystals and color.
I am sure you will be able to make the most beautiful works before long.
I reply here, because I cannot find writing board.
Thank you very much!^^

Have been imported from the previous website. 

writer: Phil Hamling

Your work is magnificent! I was mesmerized by the several different kinds of crystalline glazes you use and believe you are a true Master. If you are so inclined I would appreciate any comments you could offer on my work. I am a 1979 engineering graduate of Alfred University, where I began my involvement with crystalline glazes, and have been working steadily at it for the last 3 years. I can see I have a long way to go to get near your level of achievement.

Have been imported from the previous website.

Thank you very much for visiting our website. How was? Please leave your message~!

Have a nice day~ ^^